Síntese e Caracterização de Vidro Bioativo  (BG-58S) pela Rota Sol-Gel sem e com a  Presença de Solvente e Agente Porogênico

Veronica  C. P. F. Aguiar; Isabela S. Gonçalves; Fernando  S. Ortega; Karen   J. Santos G. Costa; Diogo  P.  Lauda; Ivone  R. Oliveira

doi:10.19142/rpq.v17i34.704

Veronica C. P. F. Aguiar Universidade do Vale do Paraíba, São José dos Campos https://orcid.org/0009-0009-8893-9672
Isabela S. Gonçalves Universidade do Vale do Paraíba, São José dos Campos https://orcid.org/0000-0002-9928-6197
Fernando S. Ortega Universidade do Vale do Paraíba, São José dos Campos https://orcid.org/0000-0001-5915-2453
Karen J. Santos G. Costa Universidade do Vale do Paraíba, São José dos Campos https://orcid.org/0000-0003-4543-9503
Diogo P. Lauda Universidade do Vale do Paraíba, São José dos Campos https://orcid.org/0000-0002-7478-5838
Ivone R. Oliveira Universidade do Vale do Paraíba, São José dos Campos https://orcid.org/0000-0002-9747-7651

DOI: https://doi.org/10.19142/rpq.v17i34.704

Palavras-chave: sol-gel, vidro bioativo BG-58S, álcool, surfactante

Resumo

Vidros bioativos como BG-58S (58 SiO2, 33 CaO, 9 P2O5, % em massa), uma vez transplantados, promovem uma reação biológica na interface do material, que estimula a proliferação celular, a resposta gênica e a formação de uma ligação com os tecidos vivos, inibindo o crescimento de bactérias devido a mudança do pH do meio. Estes, por sua vez, auxiliam na formação de uma camada biologicamente ativa de hidroxiapatita na superfície do BG. Rotas de produção do BG pelo método sol-gel tem avaliado a influência de diferentes reagentes usados na síntese nas características do pó obtido. Nesse contexto, o objetivo deste estudo foi avaliar a influência de reagentes na síntese de BG-58S a fim de obter melhores propriedades visando aplicação na regeneração óssea. Oito diferentes composições foram preparadas e variadas a fonte de fósforo (TEP ou AF), a adição ou não de solvente (etanol) e de agente porogênico (Pluronic F-127). As composições foram caracterizadas quanto à temperatura de calcinação por análise termogravimétrica, fases por difração de raios X, composição química por espectroscopia de infravermelho por transformada de Fourier, porosidade e área específica por volumetria de nitrogênio (BET). O uso do agente porogênico nas condições usadas neste trabalho não foi efetiva para a obtenção de estruturas micelares como formadoras de poros, necessitando ajustar as demais condições de processamento, permitindo a obtenção de composições mesoporosas.

Referências

1. ARIF, Z.U., MUHAMMAD YASIR KHALID, NOROOZI, R., SADEGHIANMARYAN, A., MEISAM JALALVAND, HOSSAIN, M.: Recent advances in 3D-printed polylactide and polycaprolactone-based biomaterials for tissue engineering applications. 930–968 (2022).

2. SRINIVASNAGAR, P., MANGALORE, D.K.: Department of Mechanical Engineering Department of Mechanical Engineering. 4, 6061 (2013).

3. TURNBULL, G., CLARKE, J., PICARD, F., RICHES, P., JIA, L., HAN, F., LI, B., SHU, W.: 3D bioactive composite scaffolds for bone tissue engineering. Bioact. Mater. 3, 278–314 (2018).

4. SCHÄTZLEIN, E., KICKER, C., SÖHLING, N., RITZ, U., NEIJHOFT, J., HENRICH, D., FRANK, J., MARZI, I., BLAESER, A.: 3D-Printed PLA-Bioglass Scaffolds with Controllable Calcium Release and MSC Adhesion for Bone Tissue Engineering. Polymers (Basel). 14, (2022).

5. BARROCA, N., DANIEL DA SILVA, A.L., VILARINHO, P.M., FERNANDES, M.H.V.: Tailoring the morphology of high molecular weight PLLA scaffolds through bioglass addition. Acta Biomater. 6, 3611–3620 (2010).

6. MAXIMOV, M., MAXIMOV, O.C., CRACIUN, L., FICAI, D., FICAI, A., ANDRONESCU, E.: Bioactive glass—an extensive study of the preparation and coating methods. Coatings. 11, 1–28 (2021).

7. BUI, X.V., DANG, T.H.: Bioactive glass 58S prepared using an innovation sol-gel process. Process. Appl. Ceram. 13, 98–103 (2019).

8. JONES, J.R.: Reprint of: Review of bioactive glass: From Hench to hybrids. Acta Biomater. 23, S53–S82 (2015).

9. CASAGRANDE, C.A., REPETTE, W.L.: Monitoring tetraethoxysilane hydrolysis/condensation in solutions with low alcoholic content by infrared spectroscopy. Rev. Mater. 23, (2018).

10. AIROLDI, C., DE FARIAS, R.F.: Alcóxidos como precursores na síntese de novos materiais através do processo sol-gel. Quim. Nova. 27, 84–88 (2004).

11. BAINO, F., FIUME, E., MIOLA, M., VERNÉ, E.: Bioactive solgel glasses: Processing, properties, and applications. Int. J. Appl. Ceram. Technol. 15, 841–860 (2018).

12. GHIŢULICĂ, C.D., DAMIAN-BUDA, A.I., CUCURUZ, A., VOICU, G.: Synthesis and characterization of zno(Mgo)-cao-sio2p2o5 bioglass obtained by sol-gel method in presence of surfactant agent, (2021).

13. DEKA, J.R., SONG, Y., YANG, Y.C.: The influence of isothermal aging, surfactant and inorganic precursors concentrations solidstatesciences. 2018.07.016.

14. FERNANDO, J.D.L.: Novel Mesoporous Bioactive Glasses (MBGs) as fillers in dental adhesives “Synthesis, Physico-chemical and biological evaluation”. (2018).

15. SHAH, A.T., AIN, Q., CHAUDHRY, A.A., KHAN, A.F., IQBAL, B., AHMAD, S., SIDDIQI, S.A., REHMAN, I. ur: A study of the effect of precursors on physical and biological properties of mesoporous bioactive glass. J. Mater. Sci. 50, 1794–1804 (2015).

16. XIA, W., CHANG, J.: Preparation and characterization of nanobioactive-glasses (NBG) by a quick alkali-mediated sol-gel method. Mater. Lett. 61, 3251–3253 (2007).

17. JONES, J.R.: Review of bioactive glass: From Hench to hybrids. Acta Biomater. 9, 4457–4486 (2013).

18. TODAN, L., ANGHEL, E.M., OSICEANU, P., TURCU, R.V.F., ATKINSON, I., SIMON, S., ZAHARESCU, M.: Structural characterization of some sol-gel derived phosphosilicate glasses. J. Mol. Struct. 1086, 161–171 (2015).

19. KAUR, G., PICKRELL, G., SRIRANGANATHAN, N., KUMAR, V., HOMA, D.: Review and the state of the art: Sol–gel and melt quenched bioactive glasses for tissue engineering. J. Biomed. Mater. Res. - Part B Appl. Biomater. 104, 1248–1275 (2016).

20. SIQUEIRA, R.L., ZANOTTO, E.D.: The influence of phosphorus precursors on the synthesis and bioactivity of SiO2-CaO-P2O5 sol-gel glasses and glass-ceramics. J. Mater. Sci. Mater. Med. 24, 365–379 (2013).

21. EREIBA, K.M., RABOH, A.S.A., A.G., M.: Characterization of some bioactive glasses based onSiO2–CaO–P2O5–SrO quaternary system prepared by sol–gel method. 46, 922–930 (2014).

22. KALAMPOUNIAS, A.G.: IR and Raman spectroscopic studies of sol – gel derived alkaline-earth. High Temp. 34, 299–303 (2011).

23. NARIYAL, R.K., KOTHARI, P., BISHT, B.: FTIR Measurements of SiO2 Glass Prepared by Sol-Gel Technique. Chem. Sci. Trans. 3, 1064–1066 (2014).

24. WU, C., ZHANG, Y., KE, X., XIE, Y., ZHU, H., CRAWFORD, R., XIAO, Y.: Bioactive mesopore-glass microspheres with controllable protein-delivery properties by biomimetic surface modification. J. Biomed. Mater. Res. - Part A. 95 A, 476–485 (2010).

25. SEPULVEDA, P., JONES, J.R., HENCH, L.L.: Characterization of melt-derived 45S5 and sol-gel-derived 58S bioactive glasses. J. Biomed. Mater. Res. 58, 734–740 (2001).

26. MENDES FILHO, A.A.: “Síntese e caracterização de hidroxiapatita e compósitos a partir de matéria-prima reciclada”. 181 (2006).

27. SUN, Y. SEN, LI, A.L., REN, H.H., ZHANG, X.P., WANG, C., QIU, D.: Removal of residual nitrate ion from bioactive calcium silicate through soaking. Chinese Chem. Lett. 27, 579–582 (2016).